Xrd spectra show that the bulk gan particles are wurtzite structure , and the nc gan has small domain size and the structure of solid solution phase
Xrd结果显示经由气凝法合成前后氮化镓均为一六方晶系结构，利用块状氮化镓生成的奈米粉体粒径微细且是一种固溶相结构。
By the increasing of temperature , liyco3 - xo4 was further changed into licoo2 and lixco1 - xo , and then licoo2 formed by the reaction of lixco1 - xo with li2o . the reaction that produces licoo2 is almost completely done at 700 , although some remaining li2o and li2co3 present as a partially amorphous film dispersed on the surface of licoo2 , which can accelerate the growth of licoo2 crystallites . however , when temperature is higher than 850 , some of licoo2 begin to decompose into the solid solution phase of liyco2 - yo2 and lixco1 - xo , and damaged its own crystal structure
制备licoo _ 2的合成反应中licoo _ 2的微结构不断发生变化，随着焙烧温度升高， co _ 3o _ 4晶粒逐渐减小， licoo _ 2晶粒和颗粒逐渐长大，晶格内部缺陷减少， licoo _ 2晶格趋于完整，在焙烧温度为850时licoo _ 2晶粒达到最大值；焙烧温度低于700 ，晶胞参数a随着焙烧温度上升而减小，晶胞参数c随着焙烧温度上升而增大；而高于700则晶胞参数基本保持不变。